Premium Smooth Trademark Tool Steel Wire Length 2500-5500mm Specification 6-400mm

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Steel Plate
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Bar
• Surface Treatment: Black or as Required
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Length: 2500-5500mm
• Transport Package: N/M
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7228400000
• Production Capacity: 5000ton/Month

Product Description

APPLICATION:

Our Premium Smooth Trademark Tool Steel Wire is perfectly suited for construction steel structures. Ideal for welding, riveting, and bolted assemblies, it performs exceptionally well at ambient temperatures, ensuring durability and reliability.

TECHNOLOGICAL INFORMATION:

This product is made from fully killed steel, a type of steel that is also weldable, providing superior integrity and strength.

SEMI-FINISHED PRODUCTS:

Produced from fully killed steel, our semi-finished products are also weldable, ensuring they meet the highest standards of quality and performance.

CHEMICAL COMPOSITION:

C	Mn	Si	P	S	Cr	Ni	Mo	V	Nb	Ti	Al	Cu
Max 0,20	Max 1,60	Max 0,55	Max 0,025	Max 0,025	-	-	-	-	-	-	-	Max 0,55

MECHANICAL PROPERTIES:

Effect of the cross-section on mechanical properties

Ultimate tensile strength

Thickness, mm

< 3

> 3-100

> 100-150

> 150-250

Rm, MPa

510-680

470-630

450-600

450-600

Yield stress

Thickness, mm

≤ 16

> 16-40

> 40-63

> 63-80

> 80-100

> 100-150

> 150-200

> 200-250

Re, MPa

≥ 355

≥ 345

≥ 335

≥ 325

≥ 315

≥ 295

≥ 285

≥ 275

Elongation

Thickness, mm

≤ 1

> 1-1.5

> 1.5-2

> 2-2.5

> 2.5-3

A80mm, %, longitudinal samples

≥ 14

≥ 15

≥ 16

≥ 17

≥ 18

A80mm, %, transverse samples

≥ 12

≥ 13

≥ 14

≥ 15

≥ 16

Thickness, mm

3-40

> 40-63

> 63-100

> 100-150

> 150-250

A, %, longitudinal samples

≥ 22

≥ 21

≥ 20

≥ 18

≥17

A, %, transverse samples

≥ 20

≥ 19

≥ 18

≥ 18

≥ 17

Impact test at -20°C

Thickness, mm

> 10-400 27

KV, J

TECHNOLOGICAL TREATMENT PROCESSES:

Technological treatment processes			Possible application	Temperature, °C
Hot forming	Forging		+	(1150 - 800)
	Rolling		+	(1150 - 800)
Treatment	Heat treatment	Quenching	-	-
		Tempering	-	-
	Precipitation strengthening	Supersaturation	-	-
		Ageing	-	-
	Annealing	Normalising	+	(890 - 920)
		Soft annealing	+	< 580
Thermochemical treatment	Carburising		-	-
	Other		-	-

INTERNATIONAL STEEL GRADES:

ISO		CEN		Russia
~E355-D	ISO 630:1995	S355J2G3	EN 10025:1993	~17GIS	GOST 19281 - 89
US		Japan		China
~A 706	ASTM A 706 - 00	~SM 490 A	JIS G 3106 1995	~16Mn	GB T 8164 - 93