Smooth Trademark High-Strength Steel Bar Length 2500-5500mm Specification 6-400mm

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Steel Plate
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Bar
• Surface Treatment: Black or as Required
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Length: 2500-5500mm
• Transport Package: N/M
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7228400000
• Production Capacity: 5000ton/Month

Product Description

APPLICATION:

Ideal for construction steel structures, this high-strength steel is perfect for welding, riveting, and bolted structures designed to operate efficiently at ambient temperatures. This makes it a reliable choice for a broad range of construction applications.

TECHNOLOGICAL INFORMATION:

This product features fully killed steel that ensures superior weldability and robustness, offering unparalleled performance in demanding applications.

SEMI-FINISHED PRODUCTS:

Our semi-finished products are composed of fully killed steel, ensuring excellent weldability and flexibility for further processing.

CHEMICAL COMPOSITION:

C	Mn	Si	P	S	Cr	Ni	Mo	V	Nb	Ti	Al	Cu
Max 0,20	Max 1,60	Max 0,55	Max 0,025	Max 0,025	-	-	-	-	-	-	-	Max 0,55

MECHANICAL PROPERTIES:

Effect of the cross-section on mechanical properties

Ultimate tensile strength

Thickness, mm

< 3

> 3-100

> 100-150

> 150-250

Rm, MPa

510-680

470-630

450-600

450-600

Yield stress

Thickness, mm

≤ 16

> 16-40

> 40-63

> 63-80

> 80-100

> 100-150

> 150-200

> 200-250

Re, MPa

≥ 355

≥ 345

≥ 335

≥ 325

≥ 315

≥ 295

≥ 285

≥ 275

Elongation

Thickness, mm

≤ 1

> 1-1.5

> 1.5-2

> 2-2.5

> 2.5-3

A80mm, %, longitudinal samples

≥ 14

≥ 15

≥ 16

≥ 17

≥ 18

A80mm, %, transverse samples

≥ 12

≥ 13

≥ 14

≥ 15

≥ 16

Thickness, mm

3-40

> 40-63

> 63-100

> 100-150

> 150-250

A, %, longitudinal samples

≥ 22

≥ 21

≥ 20

≥ 18

≥17

A, %, transverse samples

≥ 20

≥ 19

≥ 18

≥ 18

≥ 17

Impact test at -20°C

Thickness, mm

> 10-400 27

KV, J

TECHNOLOGICAL TREATMENT PROCESSES:

Technological treatment processes			Possible application	Temperature, °C
Hot forming	Forging		+	(1150 - 800)
	Rolling		+	(1150 - 800)
Treatment	Heat treatment	Quenching	-	-
		Tempering	-	-
	Precipitation strengthening	Supersaturation	-	-
		Ageing	-	-
	Annealing	Normalising	+	(890 - 920)
		Soft annealing	+	< 580
Thermochemical treatment	Carburising		-	-
	Other		-	-

INTERNATIONAL STEEL GRADES:

ISO		CEN		Russia
~E355-D	ISO 630:1995	S355J2G3	EN 10025:1993	~17GIS	GOST 19281 - 89
US		Japan		China
~A 706	ASTM A 706 - 00	~SM 490 A	JIS G 3106 1995	~16Mn	GB T 8164 - 93