Introduction:
Cr6WV is a medium alloy cold work mold steel with good comprehensive properties. The steel
has small deformation and good hardenability. It has good wear resistance and certain impact
toughness.
Chemical Composition
C |
Si |
Mn |
Cr |
W |
V |
P |
S |
1.00~1.15 |
≤0.40 |
≤0.40 |
5.50~7.00 |
1.10~1.50 |
0.50~0.70 |
≤0.030 |
≤0.030 |
Cr6WV Steel Physical Properties
Critical temperature of cr6wv steel
critical point |
Ac1 |
Acm |
Ar1 |
Arm |
Ms |
Mf |
Temperature (approximate) / ºC |
815 |
845 |
625 |
775 |
150 |
-100 |
Linear expansion coefficient of cr6wv steel
Temperature / ºC |
100~250 |
250~350 |
350~600 |
Expansion coefficient / ºC - 1 |
10.3×10-6 |
10.3×10-6 |
10.3×10-6 |
Heat Treatment
General annealing
The heating temperature is 830-850 degrees, the furnace is cooled to below 550 degrees,
and the furnace is air-cooled. The hardness after annealing is 229HBW.
Warm annealing process
Heating temperature 830-850 degrees, isothermal temperature 700-720 degrees. Furnace
cooling to 550 degrees air cooling, Hardness ≤ 229HBW. Annealing metallographic structure
is fine granular pearlite + carbide.
Quenched and tempered at low temperature. (960~980 degree oil quenching, 200~300 degree tempering). After tempering, it contains carbides with a mass fraction of about 8% to 10%. The
mass fraction of retained austenite is 15% to 20%.
The tempering temperature is 150~170 degrees. The hardness is 62~63HRC. The tempering temperature is 190~210 degrees. The hardness is 58~60HRC.
Features And Application
Cr6WV steel has a wide range of uses. Manufacture of molds with high mechanical strength,
wear-resistance and shock loads. Such as drill sleeves, cold mold and punches, trimming dies, stamping dies, thread rolling dies, and thread rolling plates.