1.2316 3Cr17NiMo Alloy Steel Plastic Tool Mold Steel Round Bar

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Round bar
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

Description:
Martensitic stainless chromium steel for plastic moulds, high corrosion resistance than 1.2083,
resistant to chemical attack, excellent wear resitance, uniform hardness in all dimensions, etch
grainable and easy to machine, high surface finish and polishability. Not suitable for nitriding and
chrome plating because of the high chrome content. This grade can be produced on request by
the process in hardened and tempered, soft annealed and ESR condition.

Chemical Composition(%)
 

C	Si	Mn	P	S	Cr	Ni	Mo	V
0.33-0.43	≤1.00	≤1.00	≤0.030	≤0.030	15.0-17.0	≥0.60	1.00-1.30	/

Applications :
Moulds for chemically aggressive plastics and plastics containing abrasive fillers, slit dies, profile dies,
drop forging tools, blowing moulds, mould inserts, moulds and extruding tools for corrosively acting
plastics such as PVC amino plastics and similar materials.

Physical Properties :
Density : at 20 °C 7,70 kg/dm3
Thermal expansion between : 20 °C and... °C, 10-6 m/(mK)
Thermal conductivity : at 20 °C 15,0 W/(m.K)

100 °C	200 °C	300 °C	400 °C	500 °C
10,4	10,8	11,2	11,6	11,9

Heat Treatment :
Annealing                   :  810-830°C
Hardness after annealing    :  Max. 235 HB
Stress relieving                      :  Approx. 650 °C
Hot forming   :  1050 - 850 °C
Hardening      :  1020 - 1040 °C
Quenching media:  Oil, Salt bath, Vacuum
Hardness after quenching:  48 - 52 HRC
Hardness after tempering :

100 °C	200 °C	300 °C	400 °C
52 HRC	50HRC	48HRC	49HRC