SAE 1045 4140 4340 8620 8640 ASTM Standard Q195/Q235 42CrMo Steel Billet High Carbon Steel Round Bar Billet Round Steel

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Surface: Milled/Bright/Black
• Length: 1-10m
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

Introduction:  
AISI 1045 steel Manufacturer and Exporter,supplied with round,square,flat,block,and shaft etc.AISI 1045 is defined as medium carbon steel which has 0.43%-0.5% Carbon.It offers good weldability, good machinability, high strength and impact properties,but low in hardenability because of lack of suitable alloying elements,but it can obtain surface hardnesses 54-60HRC after flame or induction hardening. AISI 1045 is generally supplied in the black hot forged or normalized condition,and has a tensile strength of 570 -700 MPa with surface hardness170-210HB.

1.Supply Form & Size & Tolerance

Supply Form	Size(mm)	Process	Tolerance
Round	Φ6-Φ100	Cold Drawn	Bright/Black	Best H11
	Φ16-Φ350	Hot Rolled	Black	-0/+1mm
			Peeled/ground	Best H11
	Φ90-Φ1000	Hot Forged	Black	-0/+5mm
			Rough Turned	-0/+3mm
Flat/Square/Block	Thickness :120-800	Hot Forged	Black	-0/+8mm
	Width:120-1500		Rough Machined	-0/+3mm

Remark:Tolerance can be customized as per requests
2.Chemical Composition

Standard	Grade	C	Si	Mn	P	S	Cr
ASTM A29	1045	0.43-0.50	-	0.60-0.90	≤0.04	≤0.05	-
EN 10083-2	C45	0.42-0.50	≤0.4	0.50-0.90	≤0.03	≤0.035	≤0.4
	1.1191
JIS G4051	S45C	0.42-0.48	0.15-0.35	0.60-0.90	≤0.03	≤0.035	-

3.Physical Property

Density, g/cm3	7.87
Melting point °C	1495
Modulus of Elasticity, psi	29 x 10^6
Coefficient of Thermal Expansion, 68-212˚F, /˚F	6.39 x 10^-6
Thermal Conductivity, Btu/ft hr ˚F	30
Specific Heat, Btu/lb ˚F	0.116
Electrical Resistivity, Microhm-in	6.42

4. Mechanical Property

Section Size mm	≤ 16	17 - 40	41 - 100
Tensile Strength Mpa	700-850	6500-800	630-780
Yield Strength Mpa	≥ 500	≥430	≥ 370
Elongation in 50mm %	≥ 14	≥ 16	≥ 17
Impact Charpy J	≥ 30	≥ 30	≥ 30
Hardness HB	210-245	195-235	185-230

Remark:Water Quench at 820°C -850°Cor oil quench at 830°C-860°C and Tempered Between 540°C - 680°C
5.Forging
Heat AISI 1045 with two steps,first heat the temperature to 750 ^oC - 800 ^oC ,hold for suitable time,then heat the temperature up to 1100 ^oC - 1200 ^oC,hold enough time for the steel to be thoroughly heated.Minimum forging temperature 850°C,so don't forge below it.AISI 1045 steel  should be cooled as slowly as possible in still air or in sand after forged.
6.Normalizing
Normalizing is used to refine the structure of forgings that might have cooled non-uniformly after forged,and considered as a conditioning treatment before final heat treatment.Normalizing temperature for AISI 1045  steel should be carried out between 870ºC-920ºC. hold suitable time for the steel to be thoroughly heated to  complete the ferrite to austenite transformation.Soak for 10 - 15 minutes,then cool in still air.
7.Annealing
Annealing  is considered as a treatment  suitable for machining.AISI 1045 should be carried our at a nominal temperature of 800ºC-850ºC,hold suitable time for the steel to be thoroughly heated, then furnace cooling.
8.Hardening
AISI 1045 may be hardened to increase surface hardness and strength.It is usually heated to temperature  820^oC - 860^oC,hold suitable time for the steel to be  heated uniformly,soak for 10 -15 minutes per 25mm of section, and quench in water or oil.Tempering should be followed  immediately after quenched.
9.Tempering
Tempering will be carried out to optimize the property after quench.AISI 1045 steel is usually heated  to 400^oC - 650^oC as required, hold until temperature is uniform throughout the section, soak for 1 hour per 25mm of section, and cool in still air.
10.Application
Compared with AISI 1020,AISI 1045 has low alloy,but can be flamed or induction hardening to obtain high strength,and is widely used in many industries which require more strength,wear resistance,
Typical applications includes Axles,Bolts, Connecting Rods, Hydraulic Clamps ,Rams, Pins , Rolls, Studs, Shafts, Spindles, Sockets, Light gears etc.