High Quality Factory Price Cr5mo1V Cold Work Alloy Tool Steel Round Bar

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Round bar
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

Introduction:  
  
The deformation of this steel due to air quenching is only about 1/4 of that of manganese-containing
oil-quenched tool steel. The wear resistance is between manganese type and high carbon and high
chromium type tool steel. Its toughness is better than anyone. It is especially suitable for tools that
require good wear resistance and special toughness. Widely used in blanking and forming dies,
rolls, punches, calendering dies and rolling dies. Also used for scissors.

Cr5Mo1V Equivalents

/	China	EU	Germany	Japan	France	England	USA
Standard	GB	EN	DIN,WNr	JIS	AFNOR	BS	-
Grade	Cr5Mo1V	X100CrMoV5 (1.2363)	X100CrMoV5-1	SKD12	Z100CDV5	BA2	A2
/	Poland	Czechia	Austria	Russia	Inter	Italy	Sweden
Standard	PN	CSN	ONORM	GOST	ISO	UNI	SS
Grade	NCLV	19571	K305	9KH5VF	X100CrMoV5	X100CrMoV5-1KU	2260

Chemical Composition

C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	V(%)	Cu(%)
0.95~1.05	≤0.50	≤1.00	≤0.030	≤0.030	4.75~5.50	≤0.20	0.90~1.40	0.15~0.50	≤0.30

Cr5Mo1V Mechanical Properties
 

Proof strength Rp0.2(MPa)	Tensile strength Rm(MPa)	Impact energy KV(J)	Elongation at fracture A(%)	Reduction in cross section on fracture Z(%)	As-Heat-Treated Condition	Brinell hardness(HBW)
828(≥)	147(≥)	21	44	22	Solution and Aging,Annealing,Ausaging,Q+T,etc	221

Heat Treatment
Annealing:
1) Slow cooling at 800-850oc
2) Spheroidizing annealing process

Tempering:
180-220oc air cooling. HRC = 60-64 510-520oc air cooling HRC = 57-60

Application
1.It is used to form elastic steel sheets with a carbon content of 0.65% to 0.80%. The hardness is
37~42HRC, and the service life can reach 110,000~120,000 times. With additional nitriding treatment,
the service life can reach 400,000 times.
2.The steel is used for wire rolling die. For machining aluminum and copper alloys.
3.It is suitable for making forming dies, blanking dies and cold blanking dies.
4.It is used to make drill sleeves, punches, trimming dies and thread rolling dies.
5.For wear-resistant plastic molds.