1.2327 Forging Steel 86crmov7 Forged Mould Tool Steel Round Bars

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Round bar
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Bar
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

Designation by Standards

 

Mat. No.	DIN	EN	AISI
1.2327	86CrMoV7	-	-

 

Chemical Composition (in weight %)

 

C	Si	Mn	Cr	Mo	Ni	V	W	Others
0.87	0.30	0.38	1.75	0.28	0.13	0.10	-	-

 

Description
Low alloyed cold working tool steel.

Applications
Cold rolls, back-up rolls, straightening rolls, non-ferrous 2 and 4 high roll mills.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: 210
Density [g/cm³]: 7.85
Thermal conductivity [W/m.K]: 35.0
Electric resistivity [Ohm mm²/m]: 0.30
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10^-6 oC^-1

 

20-100^oC	20-200^oC	20-300^oC	20-400^oC	20-500^oC
12.5	13.2	13.6	14.0	14.3

 

Continuous Cooling Transformation (CCT) Diagram

 

Time-Temperature Transformation (TTT) Diagram

 

Soft Annealing
Heat to 720-750^oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650^oC, holding for 1-2 hours at heat, followed by air cooling.
This operation is performed to reduce distortion during heat treatment.

Hardening
Harden from a temperature of 800-820^oC, 830-850^oC followed by water or oil quenching. Hardness after quenching is 64-67 HRC.

Tempering
Tempering temperature: 200-600^oC.

Tempering Temperature (^oC) vs. Hardness (HRC)

 

100^oC	200^oC	300^oC	400^oC
65	61	58	-

 

Forging
Hot forming temperature: 1150-850^oC.

Machinability
No data.

Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically
suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended
as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive
updated editions as the become available.