Smooth Steel Plate Length 2500-5500mm with Specification 6-400mm for Strength

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Steel Plate
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Bar
• Surface Treatment: Black or as Required
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Length: 2500-5500mm
• Transport Package: N/M
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7228400000
• Production Capacity: 5000ton/Month

Product Description

APPLICATION:

Introducing our exquisite Smooth Trademark Steel Sheet Plate, a marvel of engineering precision, available in an impressive range of lengths from 2500mm to 5500mm and specifications spanning 6mm to 400mm. This product is impeccably designed for the robust demands of construction steel structures. It seamlessly performs in scenarios requiring exceptional welding, as well as riveting and bolted connections, all under ambient conditions ensuring unrivaled strength and reliability.

TECHNOLOGICAL INFORMATION:

Expertly crafted from the finest fully killed steel, this product promises unparalleled weldability and steadfast reliability across a multitude of challenging applications. Its superior composition ensures it stands as a testament to durability and performance.

SEMI-FINISHED PRODUCTS:

Our semi-finished products, meticulously constructed from fully killed and weldable steel, offer an exceptional guarantee of performance and structural integrity. They are designed to meet the highest standards of quality, ensuring that every project is built to last.

CHEMICAL COMPOSITION:

C	Mn	Si	P	S	Cr	Ni	Mo	V	Nb	Ti	Al	Cu
Max 0,20	Max 1,60	Max 0,55	Max 0,025	Max 0,025	-	-	-	-	-	-	-	Max 0,55

MECHANICAL PROPERTIES:

Effect of the cross-section on mechanical properties

Ultimate tensile strength

Thickness, mm

< 3

> 3-100

> 100-150

> 150-250

Rm, MPa

510-680

470-630

450-600

450-600

Yield stress

Thickness, mm

≤ 16

> 16-40

> 40-63

> 63-80

> 80-100

> 100-150

> 150-200

> 200-250

Re, MPa

≥ 355

≥ 345

≥ 335

≥ 325

≥ 315

≥ 295

≥ 285

≥ 275

Elongation

Thickness, mm

≤ 1

> 1-1.5

> 1.5-2

> 2-2.5

> 2.5-3

A80mm, %, longitudinal samples

≥ 14

≥ 15

≥ 16

≥ 17

≥ 18

A80mm, %, transverse samples

≥ 12

≥ 13

≥ 14

≥ 15

≥ 16

Thickness, mm

3-40

> 40-63

> 63-100

> 100-150

> 150-250

A, %, longitudinal samples

≥ 22

≥ 21

≥ 20

≥ 18

≥17

A, %, transverse samples

≥ 20

≥ 19

≥ 18

≥ 18

≥ 17

Impact test at -20°C

Thickness, mm

> 10-400 27

KV, J

TECHNOLOGICAL TREATMENT PROCESSES:

Technological treatment processes			Possible application	Temperature, °C
Hot forming	Forging		+	(1150 - 800)
	Rolling		+	(1150 - 800)
Treatment	Heat treatment	Quenching	-	-
		Tempering	-	-
	Precipitation strengthening	Supersaturation	-	-
		Ageing	-	-
	Annealing	Normalising	+	(890 - 920)
		Soft annealing	+	< 580
Thermochemical treatment	Carburising		-	-
	Other		-	-

INTERNATIONAL STEEL GRADES:

ISO		CEN		Russia
~E355-D	ISO 630:1995	S355J2G3	EN 10025:1993	~17GIS	GOST 19281 - 89
US		Japan		China
~A 706	ASTM A 706 - 00	~SM 490 A	JIS G 3106 1995	~16Mn	GB T 8164 - 93