Type: | Alloy Steel Bar |
---|---|
Standard: | AISI, ASTM, DIN, JIS, GB, BS |
Composition: | Ferrous Steel Scrap |
Technique: | Forged |
Shape: | Bar |
Surface Treatment: | Machined |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Alloyed case hardening steel for the parts which require core tensile strength and high hardness. Susceptible to the large seized parts with high wearing resistance and loading such as: gears, screws, camshafts, bushings.
Steel adjusted for cutting with a cutting machine. The carburising temperature range can be higher than provided in the file (depending on the carburising process)
Steel adjusted for cutting with a cutting machine. The carburising temperature range can be higher than provided in the file (depending on the carburising process)
C | Si | Mn | P | S | Cr | Mo | Ni | B |
---|---|---|---|---|---|---|---|---|
0,15 - 0,21 | Max 0,40 | 0,50 - 0,90 | Max 0,025 | Max 0,035 | 1,50 - 1,80 | 0,25 - 0,35 | 1,40 - 1,70 | - |
Hardness after | Symbol | Value | |
Soft annealing (+A) | HB | ≤ 229 | |
Heat treatment (carburising, quenching and tempering) (+QT) | HRC | ≥ 60 | |
Ultimate tensile strength Rm, after quenching and tempering at 200 °C: | |||
Diameter, d, mm | d ≤ 16 | 16 < d ≤ 40 | 40 < d ≤ 100 |
Rm, MPa | 1160 | 1080 | 900 |
Property | Unit | Value |
Density, ρ | g·cm-3 | 7.85 |
Technological treatment processes | Possible application | Temperature, °C | ||
Hot forming | Forging | + | 1150 - 850 | |
Rolling | + | 1150 - 850 | ||
Thermochemical treatment | Carburising | + | 880 - 980 | |
Carbonitriding | + | 860 - 950 | ||
Heat treatment | Annealing | Normalising | + | 830 - 870 |
Soft annealing | + | 650 - 700 | ||
Heat treatment after carburising1) | Core hardening | + | 830 - 870 | |
Intermediate annealing | + | 630 - 650 | ||
Case hardening | + | 780 - 820 | ||
Tempering | + | 150 - 200 | ||
1) If possible, hardening has to be performed with the temperature equal or close to the heat treatment temperature |
ISO | CEN | Russia | |||
~18CrNiMo7 | ISO 683-11:1987 | 18CrNiMo7-6 | EN 10084:1998 | - | - |
US | Japan | China |