| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.87 | 0.30 | 0.38 | 1.75 | 0.28 | 0.13 | 0.10 | / | / |
Due to the high carbon content, 1.4034 is not suitable for welding. If welding cannot be avoided, preheat to 350 °C-400 °C and post heat treatment temperature is about 650 °C.
X46Cr13 has good workability when hot, and potential to reach high hardness of up to 56 HRC. It contains a moderately high carbon ratio of approximately 0.46% which gives it a good compromise between high hardness and corrosion resistance for many applications. It is also relatively inexpensive to produce.
(PREN = 12,5-14,5)
DIN EN 1.4034 is not resistant to intergranular corrosion upon delivery. It has good corrosion resistance in non-chloride and acid-base environments; polished surface under tempered condition have good corrosion resistance; in order to maintain good corrosion resistance, it is not recommended to be used in annealed or high temperature conditions.
Hardened steel for cutting tools, table knives, machine knives, razors, scissors and measuring tools, ball bearings, skates, etc.
1 Black Surface
2 Grounded: Bright but rough ; Not precision
3 Machining for plate: Bright and precision; Little turning scar
4 Peeled/Turned: Bright and precision; Little turning scar
5 Polished: Very Bright and precision size; Not turning scar