DIN 1.2419 CrWMn 105wcr6 Sks31 Alloy Steel Cold Work Tool Die Special Steel

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Round bar
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

About Product:

1.2419 is a low-alloy tool steel containing tungsten and chromium, which is characterized by a high level of hardness that
can be achieved and very good toughness. In the performance range of tungsten steels, it lies between 1.2510 and 1.2419.05.

With correct heat treatment, it achieves a maximum working hardness of 64 HRC and a higher wear resistance than 1.2510.
At the same time, it offers more toughness and "power reserves" than 1.2419.05.

The steel is equally suitable for outdoor and kitchen knives. I recommend it for all knives that should be significantly more
tough than the high-carbon steels 1.2419.05, 1.2063 and 1.2562, but at the same time should be more wear-resistant than
1.2510.Due to the overall still relatively low content of carbides, the steel is excellent for finely ground cutting edges.

CHEMICAL COMPOSITION:

C	Si	Mn	P	S	W	Cr
1.00~1.10	0.10~0.40	0.80~1.10	0.03 max	0.03 max	1.00~1.30	0.90~1.10

Physical properties of 105WCr6 | 1.2419 Tool Steel

• Density: 7.85kg/m3
• Thermal conductivity:
• Forging ratio: 4:1 Minimum
• Microstructure:
• Magnetic:

Mechanical properties of Alloy Steel 105WCr6 | 1.2419 tool steel

• Hardness: Annealling  230 HB max, Q+T: 54-64 HRC, different hardness according different Tempering temperature.
• Yield strength:

105WCr6 | 1.2419 tool steel Heat treatment:

• Annealing: Annealing temperature/ºC: 720~750; After the annealing, degree of hardness ≤HBS: 230
• Quenching: Hardening temperature/ºC: 800~830, Quenching in Oil
• Tempering: Commonly used drawing temperature/ºC: 150~250;  After tempering hardness HRC | 100 ºC : 64;
• After tempering hardness HRC | 200 ºC : 61; After tempering hardness HRC | 300 ºC : 58 ;
• After tempering hardness HRC | 400 ºC : 54
• Normalizing:at Normalizing temperature, then cool in furnace

 Forged steel properties of Cold work tool 105WCr6 | 1.2419 tool steel
For forging 105WCr6 | 1.2419 steel, Slowly Pre-heat, at Hot-working temperature/ºC: 1050~850

Processing of Steel Material 105WCr6 | 1.2419 | 56NiCrMoV7
Otai Special provides the Grinding, milling, polishing, turning, drilling, and another machining service as your required tolerances and size.

Processing of 105WCr6 | 1.2419 Steel
1.2419, DIN 105WCr6 Machining, Our production completely according to the 1.2419, DIN 105WCr6 standards to meet the 1.2419,
DIN 105WCr6 Machining, can also according to the customer request, to meet the requirements of customers of 1.2419, DIN 105WCr6 Machining.

Packing of 105WCr6 | 1.2419 tool steel
By steel Wire Bundling then put in a container, or as customer require packing.

Welding performance
1.2419, DIN 105WCr6 Welding performance, Our production completely according to the 1.2419, DIN 105WCr6 standards to meet the 1.2419, DIN 105WCr6 Welding performance, can also according to the customer request, to meet the requirements of customers of 1.2419, DIN 105WCr6 Welding performance.

Applications of 105WCr6 | 1.2419 Steel
Cutting and punching tools for sheet thickness up to 6 mm, also for paper and plastics, roll shear blades for sheet thickness up to 6 mm, small bending and drawing tools, thread cutting tools, reamers, woodworking tools, gauges and other measuring tools, small inserts, and plastic molds.