High Strength Smooth Steel Plate Length 2500-5500mm Specification 6-400mm

• Customization: Available
• Type: Alloy Steel Bar
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Steel Plate
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Bar
• Surface Treatment: Black or as Required
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Length: 2500-5500mm
• Transport Package: N/M
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7228400000
• Production Capacity: 5000ton/Month

Product Description

APPLICATION:

Discover the ultimate in construction excellence with our Smooth Trademark Steel Sheet Plate. Engineered to perfection, these plates span an impressive range of lengths from 2500mm to 5500mm and boast specifications between 6mm and 400mm, making them the ideal choice for robust construction steel structures. They are specifically designed to thrive in demanding environments, offering unparalleled performance in welding, riveting, and bolted connections at ambient temperatures.

TECHNOLOGICAL INFORMATION:

Harnessing the power of fully killed steel, our product delivers extraordinary weldability and unwavering reliability, making it a top choice for diverse applications in the modern industry.

SEMI-FINISHED PRODUCTS:

Our semi-finished products, crafted from fully killed and weldable steel, are synonymous with exceptional performance and structural integrity, ensuring they meet the highest standards in the industry.

CHEMICAL COMPOSITION:

C	Mn	Si	P	S	Cr	Ni	Mo	V	Nb	Ti	Al	Cu
Max 0,20	Max 1,60	Max 0,55	Max 0,025	Max 0,025	-	-	-	-	-	-	-	Max 0,55

MECHANICAL PROPERTIES:

Effect of the cross-section on mechanical properties

Ultimate tensile strength

Thickness, mm

< 3

> 3-100

> 100-150

> 150-250

Rm, MPa

510-680

470-630

450-600

450-600

Yield stress

Thickness, mm

≤ 16

> 16-40

> 40-63

> 63-80

> 80-100

> 100-150

> 150-200

> 200-250

Re, MPa

≥ 355

≥ 345

≥ 335

≥ 325

≥ 315

≥ 295

≥ 285

≥ 275

Elongation

Thickness, mm

≤ 1

> 1-1.5

> 1.5-2

> 2-2.5

> 2.5-3

A80mm, %, longitudinal samples

≥ 14

≥ 15

≥ 16

≥ 17

≥ 18

A80mm, %, transverse samples

≥ 12

≥ 13

≥ 14

≥ 15

≥ 16

Thickness, mm

3-40

> 40-63

> 63-100

> 100-150

> 150-250

A, %, longitudinal samples

≥ 22

≥ 21

≥ 20

≥ 18

≥17

A, %, transverse samples

≥ 20

≥ 19

≥ 18

≥ 18

≥ 17

Impact test at -20°C

Thickness, mm

> 10-400 27

KV, J

TECHNOLOGICAL TREATMENT PROCESSES:

Technological treatment processes			Possible application	Temperature, °C
Hot forming	Forging		+	(1150 - 800)
	Rolling		+	(1150 - 800)
Treatment	Heat treatment	Quenching	-	-
		Tempering	-	-
	Precipitation strengthening	Supersaturation	-	-
		Ageing	-	-
	Annealing	Normalising	+	(890 - 920)
		Soft annealing	+	< 580
Thermochemical treatment	Carburising		-	-
	Other		-	-

INTERNATIONAL STEEL GRADES:

ISO		CEN		Russia
~E355-D	ISO 630:1995	S355J2G3	EN 10025:1993	~17GIS	GOST 19281 - 89
US		Japan		China
~A 706	ASTM A 706 - 00	~SM 490 A	JIS G 3106 1995	~16Mn	GB T 8164 - 93