1.2767 Plastic Mold Steel Alloy Tool Steel Plate Sheet Mould Flat Bar

• Customization: Available
• Type: Steel Plate
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: Steel Plate
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

The Main Characteristics of DIN 1.2767/X45NiCrMo4 steel

• High toughness & hardness
• Good wear resistance
• High compressive strength
• Excellent dimensional stability
• Excellent corrosion resistance
• Good polishing and cutting performance, easy to achieve mirror effect
• Excellent hardenability, can be hardened by air cooling
• Excellent machinability

DIN 1.2767/X45NiCrMo4 STEEL SUPPLY FORM & SIZE & TOLERANCE

Hot Forged Round bar:Φ80-Φ1000mm

Hot Rolled  Round bar:Φ16-Φ130mm

Hot Forged Square bar: Max Thickness:500mm

Flat bar/Blcoks:Thickness :120-800mm ,Width:120-1500mm

Surface Finish	Black-Forged	Black-Rolled	Turned	Grinding	Polished	Peeled	Cold Drawn
Tolerance	(0,+5mm)	(0,+1mm)	(0,+3mm)	Best h9	Best h11	Best H11	Best H11

DIN 1.2767/X45NiCrMo4 STEEL CHEMICAL COMPOSITION

Grade	C	Si	Mn	P	S	Cr	Ni	Mo
1.2767	0.4-0.5	0.1-0.4	0.15-0.45	≤ 0.03	≤ 0.03	1.2-1.5	3.8-4.3	0.15-0.35

DIN 1.2767/X45NiCrMo4 RELATED STANDARD & EQUIVALENT GRADE

Europe/EN:45NiCrMo16

France/AFNOR:45NCD16

USA: 6F7

DIN 1.2767/X45NiCrMo4 STEEL FORGING

• Initial Forging Temperature:1100-1200ºC
• Final Forging Temperature:800-900ºC
• Forging Ratio:above 4:1
• Cooling Method After Forged:As high nickel tool steel,DIN 1.2767 steel should be annealed after forging.

DIN 1.2767/X45NiCrMo4 STEEL HEAT TREATMENT

• DIN 1.2767/X45NiCrMo4 Isothermal Annealing

Firstly, DIN1.2767 steel is heated to the austenitization temperature of 860°C and held for 1 hour, then cooled to 640°C at 30°C/h, held for the corresponding time, and finally cooled to room temperature with the furnace.

Generally speaking, as the isothermal time prolongs, the hardness will gradually decrease.The annealed hardness of DIN 1.2767 steel is usually below 262HB.

DIN 1.2767/X45NiCrMo4 Quenching & Tempering

Quenching Temperature:840-870ºC

Quenching Medium:oil

Tempering should be followed after quenched.Tempering twice is recommended.