S1 1.2542 5crw2si Forged Rolled Cold Work Tool Steel Round Bar

• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Polished
• Model NO.: Round bar
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

Description
5CrW2Si steel is used for manufacturing blades for cold shearing metal, shovels for scraping
wire boards, dies for cold punching and trimming, woodworking tools for periodic operations,
as well as hand or pneumatic chisels, air hammer tools, boiler tools, die holders and punches,
shears (heavy vibration), cutters (heavy vibration), concrete breakers, etc.

 

Chemical Composition(%)

C	Si	Mn	P	S	W	Cr	V
0.40-0.50	0.80-1.10	0.20-0.40	0.035 max	0.035 max	1.80-2.10	0.90-1.20	0.15-0.20

5CrW2Si Physical Properties

Mechanical Properties:

- Hardness: Annealed 255-207 HB, indentation diameter 3.8-4.2mm; Quenched ≥55 HRC

Heat Treatment Specification:

- Sample quenching temperature: 860-900°C, oil cooling.

 

5CrW2Si Delivery Condition:

- Steel is delivered in the annealed state.

 

5CrW2Si Heat Treatment Specification

High-temperature annealing specification:

- Annealing temperature: 710-740°C, after homogenization, insulation for 3-4 hours, then
furnace cooling or air cooling.

Normalizing annealing specification:

- Annealing temperature: 800-820°C, insulation for 3-4 hours, then slow cooling at ≤0°C/h
to ≤600-650°C, followed by furnace cooling.

Isothermal annealing specification:

- Annealing temperature: 750-760°C, insulation for 8-10 hours, then slow cooling at 10-20°C/h
to ≤650°C, followed by furnace cooling. Hardness: 207-235 HBW, good machinability can be obtained.

Normal quenching and tempering specification:

- Quenching temperature: 860-900°C, oil cooling, tempering temperature 250°C.

High-temperature quenching and tempering specification:

- Quenching temperature: 950°C, oil cooling, tempering temperature 250°C.

 

5CrW2Si Corresponding Grades

- Chinese GB Standard Grade: 5CrW2Si

- American AS1M/UNS Standard Grade: S1/T41901

- International Organization for Standardization (ISO) Standard Grade: 45WCrV2

- German Standard Grade (DIN): 45WCrW, Material Number 1.2542

- French NF Standard Grade: 45WCrV8

- Russian TOCT Standard Grade: 5xB2C

- Swedish SS Standard Grade: 2710

- British BS Standard Grade: BS1