AISI 1117 Low Carbon Steel Hot Rolled Bar Flat Plate

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: round bar
• Composition: Stainless Steel Scrap
• Technique: Hot Rolled
• Shape: Bar Plate Sheet
• Surface Treatment: Black or as Required
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm 2mm-25mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

AISI 1117 Carbon Steel:
1117 steel is a low carbon, high manganese steel alloy known for its excellent machinability, weldability, and case hardenability. It is often used in applications where precise machining and high surface finish are required, such as shafts, bushings, and hydraulic fittings.

Chemical Composition
Carbon (C): 0.14 - 0.20%
Manganese (Mn): 1.00 - 1.35%
Phosphorus (P): Maximum 0.040%
Sulfur (S): Maximum 0.040%

Mechanical Properties:
·Tensile Strength: 410 - 530 MPa
·Yield Strength (0.2% offset): 310 - 380 MPa
·Elongation at Break: 15 - 25%
·Reduction of Area: 40 - 50%
·Hardness (Brinell): 120 - 220 HB

Physical Properties:
·Density: 7.87 g/cm³
·Thermal Conductivity: 49.8 W/m·K (at 100°C)
·Specific Heat Capacity: 0.486 J/g·K
·Thermal Expansion: 11.5 µm/m·K (20-100°C)

Heat Treatment:
1117 steel is typically supplied in the annealed condition. It can be case hardened by carburizing or carbonitriding to improve its surface hardness and wear resistance. Heat treatment processes such as annealing, normalizing, and quenching can be applied to achieve desired mechanical properties.

Applications:
·Shafting: Used in the manufacture of shafts, axles, and crankshafts requiring good machinability and surface finish.
·Bushings and Bearings: Suitable for producing bushings, bearings, and sleeves in automotive and machinery applications.
·Hydraulic Fittings: Used to manufacture hydraulic fittings, couplings, and connectors due to its weldability and formability.
·Fasteners: Used in the production of bolts, nuts, and screws requiring good machinability and ductility.
·Automotive Parts: Components such as gears, cams, and linkages in automotive transmissions and engines.

Surface Treatment:
Surface treatments such as plating, painting, or phosphate coating can be applied to enhance corrosion resistance and improve appearance.

Quality Assurance:
Manufacturers ensure the quality of 1117 steel through chemical analysis, mechanical testing, dimensional inspection, and surface finish evaluation. Compliance with industry standards and specifications is essential to meet customer requirements.

Environmental Considerations:
1117 steel is recyclable and can be reused to produce new steel products, reducing the environmental impact associated with steel production.
Carbon (C): 0.14 - 0.20%
Manganese (Mn): 1.00 - 1.35%
Phosphorus (P): Maximum 0.040%
Sulfur (S): Maximum 0.040%

Mechanical Properties:
·Tensile Strength: 410 - 530 MPa
·Yield Strength (0.2% offset): 310 - 380 MPa
·Elongation at Break: 15 - 25%
·Reduction of Area: 40 - 50%
·Hardness (Brinell): 120 - 220 HB

Physical Properties:
·Density: 7.87 g/cm³
·Thermal Conductivity: 49.8 W/m·K (at 100°C)
·Specific Heat Capacity: 0.486 J/g·K
·Thermal Expansion: 11.5 µm/m·K (20-100°C)

Heat Treatment:
1117 steel is typically supplied in the annealed condition. It can be case hardened by carburizing or carbonitriding to improve its surface hardness and wear resistance. Heat treatment processes such as annealing, normalizing, and quenching can be applied to achieve desired mechanical properties.

Applications:
·Shafting: Used in the manufacture of shafts, axles, and crankshafts requiring good machinability and surface finish.
·Bushings and Bearings: Suitable for producing bushings, bearings, and sleeves in automotive and machinery applications.
·Hydraulic Fittings: Used to manufacture hydraulic fittings, couplings, and connectors due to its weldability and formability.
·Fasteners: Used in the production of bolts, nuts, and screws requiring good machinability and ductility.
·Automotive Parts: Components such as gears, cams, and linkages in automotive transmissions and engines.

Surface Treatment:
Surface treatments such as plating, painting, or phosphate coating can be applied to enhance corrosion resistance and improve appearance.

Quality Assurance:
Manufacturers ensure the quality of 1117 steel through chemical analysis, mechanical testing, dimensional inspection, and surface finish evaluation. Compliance with industry standards and specifications is essential to meet customer requirements.

Environmental Considerations:
1117 steel is recyclable and can be reused to produce new steel products, reducing the environmental impact associated with steel production.
Carbon (C): 0.14 - 0.20%
Manganese (Mn): 1.00 - 1.35%
Phosphorus (P): Maximum 0.040%
Sulfur (S): Maximum 0.040%

Mechanical Properties:
·Tensile Strength: 410 - 530 MPa
·Yield Strength (0.2% offset): 310 - 380 MPa
·Elongation at Break: 15 - 25%
·Reduction of Area: 40 - 50%
·Hardness (Brinell): 120 - 220 HB

Physical Properties:
·Density: 7.87 g/cm³
·Thermal Conductivity: 49.8 W/m·K (at 100°C)
·Specific Heat Capacity: 0.486 J/g·K
·Thermal Expansion: 11.5 µm/m·K (20-100°C)

Heat Treatment:
1117 steel is typically supplied in the annealed condition. It can be case hardened by carburizing or carbonitriding to improve its surface hardness and wear resistance. Heat treatment processes such as annealing, normalizing, and quenching can be applied to achieve desired mechanical properties.

Applications:
·Shafting: Used in the manufacture of shafts, axles, and crankshafts requiring good machinability and surface finish.
·Bushings and Bearings: Suitable for producing bushings, bearings, and sleeves in automotive and machinery applications.
·Hydraulic Fittings: Used to manufacture hydraulic fittings, couplings, and connectors due to its weldability and formability.
·Fasteners: Used in the production of bolts, nuts, and screws requiring good machinability and ductility.
·Automotive Parts: Components such as gears, cams, and linkages in automotive transmissions and engines.

Surface Treatment:
Surface treatments such as plating, painting, or phosphate coating can be applied to enhance corrosion resistance and improve appearance.

Quality Assurance:
Manufacturers ensure the quality of 1117 steel through chemical analysis, mechanical testing, dimensional inspection, and surface finish evaluation. Compliance with industry standards and specifications is essential to meet customer requirements.

Environmental Considerations:
1117 steel is recyclable and can be reused to produce new steel products, reducing the environmental impact associated with steel production.