Hot Forged 21crmov5-11 1.8070 Steel Flat Round Bar

• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Composition: Stainless Steel Scrap
• Technique: Forged
• Shape: Plate
• Surface Treatment: Black or as Required
• Model NO.: Round bar
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
• Application: Tool Steel Bar
• Transport Package: Wooden
• Specification: 6-400mm
• Trademark: Smooth
• Origin: China
• HS Code: 7214100000
• Production Capacity: 5000 Ton/Year

Product Description

About products

21CrMoV5-7 steel,also refers to DIN 1.7709, is defined as pearlitic heat-resistant steel with high
content Cr and Mo as per EN 10269 Standard.While 21CrMoV5-11,with higher Mo content(1%),
can be seen as an upgraded version of 21CrMov5-7 steel.

Both of them can work at around 500 degrees for a long time and are mainly used in petrochemical,
coal conversion, nuclear power, steam turbine cylinders, thermal power and other occasions with
harsh conditions and corrosive media. Main applications: rolls, boilers, reactors, heaters, steam
generation device, etc.

 

Chemical Composition(%)

C	Si	Mn	P	S	Cr	Mo	Ni	V
0.17-0.25	0.3-0.6	0.3-0.6	≤0.025	≤0.03	1.2-1.5	1.0-1.2	≤0.6	0.25-0.35

21CrMoV5-11 STEEL FORGING

• Initial Forging Temperature:1100ºC
• Final Forging Temperature:850ºC
• Forging Ratio:above 4:1
• Post-Forging Treatment:21CrMoV5-11 / 21CrMoV5-7 steel,as high Cr-Mo steel, is prone to cracks due to improper cooling after forged,so the recommended method is to arrange annealing heat treatment immediately after forged,the purpose is to slowly cool the material and eliminate the huge internal stress after forging.

21CrMoV5-11 STEEL HEAT TREATMENT

21CrMoV5-11 Steel High Temperature Tempering

The recommended high temperature tempering temperature of 21CrMoV5-11/21CrMoV5-7 steel is 690-710 ºC, air cooling, and the surface hardness of the material after tempering is not greater than 241HB.

21CrMoV5-11 Steel Quenching & Tempering(QT)

• Quenching Temperature:930-950ºC
• Quenching Medium:Oil
• Tempering Temperature:700-740ºC